priti®multidisc ZrO2 monochrome High Translucent

For all milling machines that accept round blanks with a diameter of 98.5 mm

priti®multidisc ZrO2 High Translucent is the material of choice for the most vibrant, highest aesthetics on restorations with up to three pontics.

(5Y-TZP) available in monochrome in 16 VITA® shades and white, 49% translucence, flexural strength > 650 MPa

INDICATION

You can use priti®multidisc ZrO2 High Translucent to fabricate inlays, onlays, veneers, partial crowns, anatomically reduced and monolithic, fully anatomical crowns and bridges (up to three pontics) for anterior and posterior areas. The discs are available in white and pre-stained in the 16 VITA® shades. Translucence is comparable to that of lithium disilicate. Its high translucence mean the material is particularly suitable for fabrication of non-veneered restorations.

MATERIAL

  • Zirconium dioxide Type II, Class 4 (DIN EN ISO 6872)
  • Flexural strength > 650 MPa
  • High translucence of 49%
  • Brilliant aesthetics
  • CTE 10 ·10-6 · K-1
  • Thin wall thicknesses of 0.4 mm for single crowns in the anterior tooth area and 0.6 mm in the posterior tooth area
  • Precise edges and margins due to highly compacted material
  • Veneering possible with any ceramic mapped to the CTE of ZrO2
  • Cross-batch color fidelity
  • Homogeneous block shading
  • Color can be reproduced at any time
  • Biocompatible

CHEMICAL COMPOSITION

Zirconium dioxide (ZrO2/HfO2): 89.89 - 90.7 %
Yttrium oxide (Y2O3): 8.55 - 10.11 %
Aluminum oxide (Al2O3): < 0.2 %
Other oxides: < 0.7 %

CONSTRUCTION

Systems must be constructed of the following specifications: CrownsMaryland-bridges3-unit bridges
Minimum framework thicknessanterior0.4 mm0.4 mm0.6 mm
Minimum framework thicknessposterior0.6 mm0.6 mm0.6 mm
Connectorsanterior 6 mm²6 mm²
Connectorsposterior 9 mm²9 mm²
Framework designAnatomically shaped (supporting veneer ceramics); fully anatomical

SINTERING

Recommendation for standard sintering:
Heating and cooling rate 10°C/min
Hold time 120 minutes at 1,450°C
Total sintering time approx. 7 hours

Recommendation on rapid sintering: (for bridges with up to 3 pontics)
Heating rate 10°C/min
Hold time 30 minutes at 1,500°C
Cooling rate 40°C/min
Total sintering time approx. 4 hours

Sintering together with other materials could cause unwanted changes in color and translucence. This applies particularly to materials processed using dye liquids. Sintering beads must also be replaced to avoid dye liquid residues.

It is particularly important to clean sintering furnaces that are contaminated by dye liquids before sintering a pre-shaded material for the first time. This prevents unpleasant surprises and allows optimum photo-optical results for the zirconium dioxide.


VENEERING

Any ceramic veneers recommended for zirconium dioxide ceramics may be used.

MILLING

Reduce feed rates during rough machining: The quality of milling depends on several factors including the machine, machining strategy, zirconium dioxide, etc. To ensure that you can achieve optimum milling results from the start with high translucence blanks, we recommend using a lower speed than with opaque materials during rough machining.

JobRough machining
Occlusal/cavity
Rough machining
Residual material
Tool diameter2.5 mm 1.0 mm
Parameter:
Spindle speed20,000-22,000 rpm20,000-22,000 rpm
Feed rate1,200-1,500 mm/min1,000-1,300 mm/min
Infeed rate 1,000 mm/min700 mm/min
Allowance0.15 mm0.15 mm
Tool path distance1.00 mm0.20 mm
Step down/step over1.00 mm0.50 mm

Coated milling tools: These offer the benefit of low wear with longer tool life.


ADJUSTMENTS

Any adjustments required to the sintered restorations once compacted must only be carried out using diamond-coated tools to prevent damage to the material caused by local overheating or exposure of the surface of the restoration to excessive force.


FIXING

Restorations can be cemented conventionally with a zinc phosphate or glass ionomer cement or with self-adhesive and fully-adhesive fixing material.

VARIANTS

HightA1A2A3A3,5A4B1B2B3B4C1C2C3C4D2D3D4white
10 mm13107-D985-10A1HT13107-D985-10A2HT13107-D985-10A3HT13107-D985-10A35HT13107-D985-10A4HT13107-D985-10B1HT13107-D985-10B2HT13107-D985-10B3HT13107-D985-10B4HT13107-D985-10C1HT13107-D985-1OC2HT13107-D985-10C3HT13107-D985-1OC4HT13107-D985-10D2HT13107-D985-10D3HT13107-D985-10D4HT13107-D985-10HT
12 mm13107-D985-12A1HT13107-D985-12A2HT13107-D985-12A3HT13107-D985-12A35HT13107-D985-12A4HT13107-D985-12B1HT13107-D985-12B2HT13107-D985-12B3HT13107-D985-12B4HT13107-D985-12C1HT13107-D985-12C2HT13107-D985-12C3HT13107-D985-12C4HT13107-D985-12D2HT13107-D985-12D3HT13107-D985-12D4HT13107-D985-12HT
14 mm13107-D985-14A1HT13107-D985-14A2HT13107-D985-14A3HT13107-D985-14A35HT13107-D985-14A4HT13107-D985-14B1HT13107-D985-14B2HT13107-D985-14B3HT13107-D985-14B4HT13107-D985-14C1HT13107-D985-14C2HT13107-D985-14C3HT13107-D985-14C4HT13107-D985-14D2HT13107-D985-14D3HT13107-D985-14D4HT13107-D985-14HT
16 mm13107-D985-16A1HT13107-D985-16A2HT13107-D985-16A3HT13107-D985-16A35HT13107-D985-16A4HT13107-D985-16B1HT13107-D985-16B2HT13107-D985-16B3HT13107-D985-16B4HT13107-D985-16C1HT13107-D985-16C2HT13107-D985-16C3HT13107-D985-16C4HT13107-D985-16D2HT13107-D985-16D3HT13107-D985-16D4HT13107-D985-16HT
18 mm13107-D985-18A1HT13107-D985-18A2HT13107-D985-18A3HT13107-D985-18A35HT13107-D985-18A4HT13107-D985-18B1HT13107-D985-18B2HT13107-D985-18B3HT13107-D985-18B4HT13107-D985-18C1HT13107-D985-18C2HT13107-D985-18C3HT13107-D985-18C4HT13107-D985-18D2HT13107-D985-18D3HT13107-D985-18D4HT13107-D985-18HT
20 mm13107-D985-20A1HT13107-D985-20A2HT13107-D985-20A3HT13107-D985-20A35HT13107-D985-20A4HT13107-D985-20B1HT13107-D985-20B2HT13107-D985-20B3HT13107-D985-20B4HT13107-D985-20C1HT13107-D985-20C2HT13107-D985-20C3HT13107-D985-20C4HT13107-D985-20D2HT13107-D985-20D3HT13107-D985-20D4HT13107-D985-20HT
25 mm13107-D985-25A1HT13107-D985-25A2HT13107-D985-25A3HT13107-D985-25A35HT13107-D985-25A4HT13107-D985-25B1HT13107-D985-25B2HT13107-D985-25B3HT13107-D985-25B4HT13107-D985-25C1HT13107-D985-25C2HT13107-D985-25C3HT13107-D985-25C4HT13107-D985-25D2HT13107-D985-25D3HT13107-D985-25D4HT13107-D985-25HT

What our customers say about us.

"pritidenta systematized zirconia for success.
Very few of the zirconia blanks on the market stand out as unique. pritidenta found a way with excellent, natural-looking results through CAM techniques. Nesting high or low is not new, of course, but nobody has gone this far to make sure the end results are consistent and predictable..."

 

Read more