priti®multidisc ZrO2 monochrome Opaque

For all open milling machines that accept round blanks with a diameter of 98.5 mm

priti®multidisc ZrO2 Opaque is perfect for robust work such as copings with up to 16 pontics, for covering discolored stumps and metal structures.

(3Y-TZPA) available in monochrome in 16 VITA® shades and white, 35% translucence, flexural strength > 1,150 MPa


You can use priti®multidisc ZrO2 Opaque to fabricate partially or fully veneered crowns and bridges (up to 16 pontics) and custom anterior and posterior suprastructures on natural abutment teeth and implants. Its low translucence means it has a strong masking effect. This material is therefore specially suitable for veneering on discolored stumps and metal structures.


  • Zirconium dioxide Type II, Class 5 (DIN EN ISO 6872)
  • Flexural strength > 1,150 MPa
  • Translucence of 35%
  • CTE (10,5 ± 0,5) ·10-6·K-1
  • Thin wall thicknesses of 0.4 mm for single crowns in the anterior tooth area and 0.6 mm in the posterior tooth area
  • Precise edges and margins due to highly compacted material
  • Veneering possible with any ceramic mapped to the CTE of ZrO2
  • Cross-batch color fidelity
  • Homogeneous block shading
  • Color can be reproduced at any time
  • Biocompatible


Zirconium dioxide (ZrO2/HfO2): 94.1 - 94.65 %
Yttrium oxide (Y2O3): 4.65 - 5.95 %
Aluminum oxide (Al2O3): < 0.4 %
Other oxides: < 0.7 %


Systems must be constructed of the following specifications: CrownsMaryland-bridges3-unit bridges
Minimum framework thicknessanterior0.4 mm0.4 mm0.6 mm
Minimum framework thicknessposterior0.6 mm0.6 mm0.6 mm
Connectorsanterior 6 mm²6 mm²
Connectorsposterior 9 mm²9 mm²
Framework designAnatomically shaped (supporting veneer ceramics); fully anatomical


Recommendation for standard sintering:
Heating and cooling rate 10°C/min
Hold time 120 minutes at 1,450°C
Total sintering time approx. 7 hours

Recommendation on rapid sintering: (for bridges with up to 3 pontics)
Heating rate 10°C/min
Hold time 30 minutes at 1,500°C
Cooling rate 40°C/min
Total sintering time approx. 4 hours

Sintering together with other materials could cause unwanted changes in color and translucence. This applies particularly to materials processed using dye liquids. Sintering beads must also be replaced to avoid dye liquid residues.

It is particularly important to clean sintering furnaces that are contaminated by dye liquids before sintering a pre-shaded material for the first time. This prevents unpleasant surprises and allows optimum photo-optical results for the zirconium dioxide.


Any ceramic veneers recommended for zirconium dioxide ceramics may be used.


Reduce feed rates during rough machining: The quality of milling depends on several factors including the machine, machining strategy, zirconium dioxide, etc. To ensure that you can achieve optimum milling results from the start with high translucence blanks, we recommend using a lower speed than with opaque materials during rough machining.

JobRough machining
Rough machining
Residual material
Tool diameter2.5 mm 1.0 mm
Spindle speed20,000-22,000 rpm20,000-22,000 rpm
Feed rate1,200-1,500 mm/min1,000-1,300 mm/min
Infeed rate 1,000 mm/min700 mm/min
Allowance0.15 mm0.15 mm
Tool path distance1.00 mm0.20 mm
Step down/step over1.00 mm0.50 mm

Coated milling tools: These offer the benefit of low wear with longer tool life.


Any adjustments required to the sintered restorations once compacted must only be carried out using diamond-coated tools to prevent damage to the material caused by local overheating or exposure of the surface of the restoration to excessive force.


Restorations can be cemented conventionally with a zinc phosphate or glass ionomer cement or with self-adhesive and fully-adhesive fixing material.


10 mmxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxx13107-D985-10*
12 mmxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxx13107-D985-12*
14 mm13107-D985-14A1*13107-D985-14A2*13107-D985-14A3*13107-D985-14A35*13107-D985-14A4*xxx13107-D985-14B2*xxxxxxxxx13107-D985-14C2*xxxxxx13107-D985-14D2*xxxxxx13107-D985-14*
16 mmxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxx13107-D985-16*
18 mmxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxx13107-D985-18*
20 mm13107-D985-20A1*13107-D985-20A2*13107-D985-20A3*13107-D985-20A35*13107-D985-20A4*xxx13107-D985-20B2*xxxxxxxxx13107-D985-20C2*xxxxxx13107-D985-20D2*xxxxxx13107-D985-20*
25 mmxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxxx13107-D985-25*

*Items in stock

Notice: All other items are deliverable on request (min. 300 pieces)... approx. an 6 week delivery period