priti®multidisc ZrO2 multicolor Translucent

For all open milling machines that accept round blanks with a diameter of 98.5 mm

priti®multidisc ZrO2 multicolor Translucent is the flexible choice for robust, authentic fully anatomical, monolithic and partially/fully veneered restorations with up to 16 pontics.

(3Y-TZP) available in 7 color gradients, 40% translucence, flexural strength > 1,150 MPa
Adjusting the position in the same disc allows all 16 Vita shades to be achieved with just 7 blanks!


You can use priti®multidisc ZrO2 multicolor Translucent to fabricate partial crowns, monolithic, fully anatomical and partially or fully veneered crowns and bridges (up to 16 pontics) and custom anterior and posterior suprastructures on natural abutment teeth and implants. The material combines very high flexural strength with good translucence. It is therefore particularly recommended as a scaffold material for aesthetic veneering.


  • Zirconium dioxide Type II, Class 5 (DIN EN ISO 6872)
  • Flexural strength > 1,150 MPa
  • High translucence of 40%
  • High aesthetics
  • CTE (10,5 ± 0,5) ·10-6·K-1
  • Thin wall thicknesses of 0.4 mm for single crowns in the anterior tooth area and 0.6 mm in the posterior tooth area
  • Precise edges and margins due to highly compacted material
  • Veneering possible with any ceramic mapped to the CTE of ZrO2
  • Cross-batch color fidelity
  • Homogeneous block shading
  • Color can be reproduced at any time
  • Biocompatible


Zirconium dioxide (ZrO2/HfO2): 94.1 - 94.65 %
Yttrium oxide (Y2O3): 4.65 - 5.95 %
Aluminum oxide (Al2O3): < 0.4 %
Other oxides: < 0.7 %


Systems must be constructed of the following specifications: CrownsMaryland-bridges3-unit bridges
Minimum framework thicknessanterior0.4 mm0.4 mm0.6 mm
Minimum framework thicknessposterior0.6 mm0.6 mm0.6 mm
Connectorsanterior 6 mm²6 mm²
Connectorsposterior 9 mm²9 mm²
Framework designAnatomically shaped (supporting veneer ceramics); fully anatomical


Recommendation for standard sintering:
Heating and cooling rate 10°C/min
Hold time 120 minutes at 1,450°C
Total sintering time approx. 7 hours

Recommendation on rapid sintering: (for bridges with up to 3 pontics)
Heating rate 10°C/min
Hold time 30 minutes at 1,500°C
Cooling rate 40°C/min
Total sintering time approx. 4 hours

Sintering together with other materials could cause unwanted changes in color and translucence. This applies particularly to materials processed using dye liquids. Sintering beads must also be replaced to avoid dye liquid residues.

It is particularly important to clean sintering furnaces that are contaminated by dye liquids before sintering a pre-shaded material for the first time. This prevents unpleasant surprises and allows optimum photo-optical results for the zirconium dioxide.


Any ceramic veneers recommended for zirconium dioxide ceramics may be used.


Reduce feed rates during rough machining: The quality of milling depends on several factors including the machine, machining strategy, zirconium dioxide, etc. To ensure that you can achieve optimum milling results from the start with high translucence blanks, we recommend using a lower speed than with opaque materials during rough machining.

JobRough machining
Rough machining
Residual material
Tool diameter2.5 mm 1.0 mm
Spindle speed20,000-22,000 rpm20,000-22,000 rpm
Feed rate1,200-1,500 mm/min1,000-1,300 mm/min
Infeed rate 1,000 mm/min700 mm/min
Allowance0.15 mm0.15 mm
Tool path distance1.00 mm0.20 mm
Step down/step over1.00 mm0.50 mm

Coated milling tools: These offer the benefit of low wear with longer tool life.


Any adjustments required to the sintered restorations once compacted must only be carried out using diamond-coated tools to prevent damage to the material caused by local overheating or exposure of the surface of the restoration to excessive force.


Restorations can be cemented conventionally with a zinc phosphate or glass ionomer cement or with self-adhesive and fully-adhesive fixing material.


The positioning and color mapping can be adjusted to the right blank height depending on restoration height:

pritidenta ShadesVITA Code
A light A1-A3
A darkA3,5-A4
B lightB1-B2
B darkB3-B4
C lightC1-C2
C darkC3-C4
D lightD2-D4

HightA lightA darkB lightB darkC lightC darkD light
14 mm13107-D985-14ALT13107-D985-14ADT13107-D985-14BLT13107-D985-14BDT13107-D985-14CLT13107-D985-14CDT13107-D985-14DLT
18 mm13107-D985-18ALT13107-D985-18ADT13107-D985-18BLT13107-D985-18BDT13107-D985-18CLT13107-D985-18CDT13107-D985-18DLT
20 mm13107-D985-20ALT13107-D985-20ADT13107-D985-20BLT13107-D985-20BDT13107-D985-20CLT13107-D985-20CDT13107-D985-20DLT
25 mm13107-D985-25ALT13107-D985-25ADT13107-D985-25BLT13107-D985-25BDT13107-D985-25CLT13107-D985-25CDT13107-D985-25DLT

What our customers say about us.

"pritidenta systematized zirconia for success.
Very few of the zirconia blanks on the market stand out as unique. pritidenta found a way with excellent, natural-looking results through CAM techniques. Nesting high or low is not new, of course, but nobody has gone this far to make sure the end results are consistent and predictable..."


Read more